D3 Steel CR12 Round And Rectangular Bar

Leading Wholesale Trader of d3 steel cr12 forged round bar and d3 steel cr12 rectangular bars from Pune.

D3 Steel Cr12 Forged Round Bar

REQUEST CALLBACK

Click to Zoom

Get Best Quote

Approx. 200 / Kilogram Get Latest Price

Product Brochure

Product Details:

Minimum Order Quantity	100 Kilogram
Material	Steel
Shape	Round
Application	Automobile Industry
Brand	Almas
Test Certificate	Lab Tc
Usage/Application	Manufacturing
Single Piece Length	6 meter
Thickness/Diameter	1-2 inch, 0-1 inch, 2-3 inch
Technique	Forged
Length	2-6 Feet

Chemical composition: The following table shows the chemical composition of HCHCR steel:

Element	C	Si	Mn	P	S	Cr	Ni	V	Cu	W
Content (%)	2.00-2.35	0.60	0.60	0.03	0.03	11.00-13.50	0.30	1.00	0.02	1.00

Mechanical Properties:

Properties	Metric	Imperial
Izod impact unnotched	28.0 J	20.7 ft-lb
Poisson’s ratio	0.27-0.30	0.27-0.30
Elastic modulus	190-210 GPa	27557-30457 ksi

Hardness: Hardness in the range 58-64 HRC. Heat treatment: Heat treatment temperatures, including rate of heating, cooling and soaking times will vary due to factors such as the shape and size of each steel component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Hardening: It is preferable to heat the tools in a controlled atmosphere. If this is not possible, pack hardening is recommended. A reducing atmosphere is desirable. Pre heat the component to 750-800°C. and allow to soak at this temperature. Raise to the hardening temperature of 950-980°C. Soak thoroughly at the temperature for thirty minutes per 25mm of ruling section, then cool or quench accordingly. Tempering: Double tempering is recommended. Tempering should be done with the least possible delay after hardening, preferably when the tools are still hand warm. Select a suitable tempering temperature, bearing in mind the service requirements. Heat slowly and uniformly. When the component has reached the desired temperature, soak for at least one hour per 25mm of thickness. The second tempering should be a repetition of the first.

Temperature [°C]	150	200	300	400	500
Hardness [HRc]	64-63	62-61	60-59	59-58	56-55

Physical Properties: Physical properties of HCHCR tool steels are given below:

Properties	Metric	Imperial
Density	7.7 x 1000 kg/m³	0.278 lb/in³
Melting point	1421°C	2590°F

Additional Information:

Item Code: HCHCRROUND
Pay Mode Terms: Thirty Percent Advance Balance Before Delivery
Port of Dispatch: PUNE
Production Capacity: 10000kgs
Delivery Time: 1-3 DAYS
Packaging Details: AS PER CUSTOMER REQUIREMENT

Yes! I am Interested

D3 Steel Cr12 Rectangular Bars