Product Details:
| Application | Automobile Industry |
| Brand | Almas |
| Technique | Cold Drawn |
| Grade | D2-1.2379 |
| Length | 2-6 Feet |
| Shape | Rectangular |
| Application | Tools used for a long time, wear resistance is very important, such as cutting or forming dies and teeth. |
| Chemical Composition | -C: 1.50-1.60 -Cr: 11.0-12.0 -Mn: 0.15-0.45 -P: ≤0.030 -S: ≤0.030 -Si: 0.10-0.40 -V: 0.90-1 |
| Equivalent Materials | ASTM A681 AISI D2, NI KU, B.S. BD 2, JIS SKD11, FED QQ-T-570, SAE J437, SAE J438, UNS T30402, GB Cr12Mo1V1 Cr12MoV |
| Heat Treatment | -After tempering hardness HRC | 100 ℃: 63 -After tempering hardness HRC | 200 ℃: 61 -After tempering hardness HRC | 300 ℃: 59 -After tempering hardness HRC | 400 ℃: 58 -Annealing: Heat to 871~898ºC, Then slowly cooling at 4.4ºC per hour or less in heat treatment furnace. -Forged: Slowly Heat to 1065ºC~954ºC for Forging the 1.2379 cold work tool steel. No forge below 926ºC. -Quenching & Tempering: For get better Mechanical properties of 1.2379 steel, Q+T the steel material is necessary. 1.2379 Tool steels Quenching \nat 1020～1040ºC, cool in oil or air; Tempering at 180～250ºC. |
Additional Information:
Product Details:
| Material Grade | D2 |
| Usage/Application | Automobile Industry |
| Shape | Flat |
| Alloy | With Alloy |
| Brand | Almas |
| Material | Steel |
| Grade | Cr12Mo1V1 |
| Surface Condition | BLACK |
| Length | 2-6 Feet |
| ASTM Standards | A681 |
| Application | Used for tools requiring long-term wear resistance, such as cutting or forming dies and teeth |
| Chemical Composition | -C: 1.50-1.60 -Cr: 11.0-12.0 -Mn: 0.15-0.45 -P: ≤0.030 -S: ≤0.030 -Si: 0.10-0.40 -V: 0.90-1 |
| Equivalent Materials | ASTM A681 AISI D2, NI KU, B.S. BD 2, JIS SKD11, FED QQ-T-570, SAE J437, SAE J438, UNS T30402, GB Cr12Mo1V1 Cr12MoV |
| Heat Treatment | Forged - Heat to 1065ºC~954ºC for forging, no forge below 926ºC, Annealing - Heat to 871~898ºC, then slowly cool at 4.4ºC per hour or less, Quenching & Tempering - Quench at 1020-1040ºC, temper at 180-250ºC |
| Material Type | Alloy Steel |
| Mechanical Properties | -Elastic modulus: 190-210 GPa -Hardness, Knoop: 769 -Hardness, Rockwell C: 62 -Hardness, Vickers: 748 -Izod impact unnotched: 77.0 J -Poisson’s ratio: 0.27-0.30 |
| Physical Properties | -Density: 7.7 x 1000 kg/m3 -Melting point: 1421°C |
Additional Information: